Hydrogen and helium bubbles in silicon
By G. Cerofolini, F. Corni, S. Frabboni, C. Nobili, G. Ottaviani, R. Tonini. 2000
136 citations recorded by the source corpus.
Abstract Hydrogen is a quite common impurity in semiconductor-silicon technology: it is unintentionally but unavoidably added to the silicon after crystal growth during wafer processing, and continues to be present during wet oxidation, film depositions, etching and annealing steps. The effects of hydrogen in single crystal silicon at low concentration have been the subject of many papers, books and conference proceedings. Much less considered is the case of hydrogen at massive concentration. One final effect of heavy hydrogen loading is the formation of cavities and bubbles, with size up to 100 nm. Cavities and bubbles are also observed after helium loading by high-fluence ion implantation. This article reviews the basic mechanisms responsible for the formation and growth of such structures in single-crystalline silicon. In particular, starting from the loading (ion implantation) and having in mind the formation of the cavities, this paper will cover: the effects of substrate temperature, the interaction of vacancies and self-interstitials with the impurity, the mechanisms of gas segregation inside the cavities, the pressure which arises because of the segregation and the subsequent displacement field in the crystal, the stability against heat treatments of the gas in the cavities and of the cavities themselves. The understanding of the physical processes should lead to gain more insight in the processes of cleavage of the Si–Si bond and vacancy agglomeration which can induce not only the formation of cavities and bubbles, but also planar cutting or explosion.
Subfields: Electrical and Electronic Engineering
View Paper: https://www.semanticscholar.org/paper/44f1f20a5e5992aa402de96bc3b9c6adb913131e
How researchers see this paper
The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.
- U. Gösele
- O. Moutanabbir
Citations in the corpus
- Heterogeneous Integration of Compound Semiconductors (2010, background): “From a thermodynamics viewpoint, the limited solubility of the implanted species in most materials provokes their segregation into cavities that grow and coalesce at high temperatures (145, 146).”