Solution-cast metal oxide thin film electrocatalysts for oxygen evolution.

By Lena Trotochaud, James K. Ranney, Kerisha N. Williams, S. Boettcher. Journal of the American Chemical Society, 2012

1,390 citations recorded by the source corpus.

Water oxidation is a critical step in water splitting to make hydrogen fuel. We report the solution synthesis, structural/compositional characterization, and oxygen evolution reaction (OER) electrocatalytic properties of ~2-3 nm thick films of NiO(x), CoO(x), Ni(y)Co(1-y)O(x), Ni(0.9)Fe(0.1)O(x), IrO(x), MnO(x), and FeO(x). The thin-film geometry enables the use of quartz crystal microgravimetry, voltammetry, and steady-state Tafel measurements to study the electrocatalytic activity and electrochemical properties of the oxides. Ni(0.9)Fe(0.1)O(x) was found to be the most active water oxidation catalyst in basic media, passing 10 mA cm(-2) at an overpotential of 336 mV with a Tafel slope of 30 mV dec(-1) with oxygen evolution reaction (OER) activity roughly an order of magnitude higher than IrO(x) control films and similar to the best known OER catalysts in basic media. The high activity is attributed to the in situ formation of layered Ni(0.9)Fe(0.1)OOH oxyhydroxide species with nearly every Ni atom electrochemically active. In contrast to previous reports that showed synergy between Co and Ni oxides for OER catalysis, Ni(y)Co(1-y)O(x) thin films showed decreasing activity relative to the pure NiO(x) films with increasing Co content. This finding is explained by the suppressed in situ formation of the active layered oxyhydroxide with increasing Co. The high OER activity and simple synthesis make these Ni-based catalyst thin films useful for incorporating with semiconductor photoelectrodes for direct solar-driven water splitting or in high-surface-area electrodes for water electrolysis.

Subfields: Electrical and Electronic Engineering, Materials Chemistry, Renewable Energy, Sustainability and the Environment

View Paper: https://www.semanticscholar.org/paper/f996bbadf2af7f336dcc18930457ff67482f2c07

How researchers see this paper

The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.

In Electrical and Electronic Engineering

  1. Ming Gong
  2. Hongjie Dai
  3. Xiaoming Sun
  4. Hailiang Wang

In Materials Chemistry

  1. Ming Gong
  2. Hongjie Dai
  3. Zhuang Liu
  4. Phaedon Avouris
  5. Kevin D. Welsher
  6. Frank Schwierz
  7. Eric Pop
  8. John Tze-Wei Yeow

In Renewable Energy, Sustainability and the Environment

  1. Ming Gong
  2. Hongjie Dai