Oxygen Release and Its Effect on the Cycling Stability of LiNixMnyCozO2 (NMC) Cathode Materials for Li-Ion Batteries

By Roland Jung, Michael Metzger, F. Maglia, C. Stinner, H. Gasteiger. 2017

1,082 citations recorded by the source corpus.

Layered LiNi x Mn y Co z O 2 (NMC) is a widely used class of cathode materials with LiNi 1/3 Mn 1/3 Co 1/3 O 2 (NMC111) being the most common representative. However, Ni-rich NMCs are more and more in the focus of current research due to their higher speciﬁc capacity and energy. In this work we will compare LiNi 1/3 Mn 1/3 Co 1/3 O 2 (NMC111), LiNi 0.6 Mn 0.2 Co 0.2 O 2 (NMC622), and LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC811) with respect to their cycling stability in NMC-graphite full-cells at different end-of-charge potentials. It will be shown that stable cycling is possible up to 4.4 V for NMC111 and NMC622 and only up to 4.0 V for NMC811. At higher potentials, signiﬁcant capacity fading was observed, which was traced back to an increase in the polarization of the NMC electrode, contrary to the nearly constant polarization of the graphite electrode. Furthermore, we show that the increase in the polarization occurs when the NMC materials are cycled up to a high-voltage feature in the dq/dV plot, which occurs at ∼ 4.7 V vs. Li/Li + for NMC111 and NMC622 and at ∼ 4.3 V vs. Li/Li + for NMC811. For the latter material, this feature corresponds to the H2 → H3phasetransition.Contrarytothecommonunderstandingthattheelectrochemical oxidationofcarbonateelectrolytescausesthe CO 2 and CO evolution at potentials above 4.7 V vs. Li/Li + , we believe that the observed CO 2 and CO are mainly due to the chemical reaction of reactive lattice oxygen with the electrolyte. This hypothesis is based on gas analysis using On-line Electrochemical Mass Spectrometry (OEMS), by which we prove that all three materials release oxygen from the particle surface and that the oxygen evolution coincides with the onset of CO 2 and CO evolution. Interestingly, the onsets of oxygen evolution for the different NMCs correlate well with the high-voltage redox feature at ∼ 4.7 V vs. Li/Li + for NMC111 and NMC622 as well as at ∼ 4.3 V vs. Li/Li + for NMC811. To support this hypothesis, we show that no CO 2 or CO is evolved for the LiNi 0.43 Mn 1.57 O 4 (LNMO) spinel up to 5 V vs. Li/Li + , consistent with the absence of oxygen release. Lastly, we demonstrate by the use of 13 C labeled conductive carbon that it is the electrolyte rather than the conductive carbon which is oxidized by the released lattice oxygen. Taking these ﬁndings into consideration, a mechanism is proposed for the reaction of released lattice oxygen with ethylene carbonate yielding CO 2 , CO, and H 2 O. © 2017. ECS. This an the terms the Attribution stability in full-cells with graphite anodes. Through an evaluation of the anode and cathode polarization in a three-electrode set-up, we conclude that the capacity fading at high voltages is due to the NMC electrode rather than the graphite electrode. By means of On-line Electrochemical Mass Spectrometry (OEMS) we prove that at high degrees of delithiation all three NMC materials release oxygen already at room temperature. The onset of the oxygen evolution corresponds well with the onset of the formation of CO 2 and which is typically assigned to electrochemical electrolyte oxidation, raising the question whether the evolution of O 2 actually causes the observed CO 2 and CO evolution. This question as well as the consequences of the oxygen release on the polarization and the cycling stability will be discussed with the experimental ﬁndings presented in this work.

Subfields: Automotive Engineering, Electrical and Electronic Engineering

View Paper: https://www.semanticscholar.org/paper/efe4ca2a05b3025070021f9db65f76242280f72d

How researchers see this paper

The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.

In Automotive Engineering

In Electrical and Electronic Engineering

Citations in the corpus

A review of the degradation mechanisms of NCM cathodes and corresponding mitigation strategies (2023, background): “However, experimental results of lattice parameter change, oxygen evolution, and capacity fade demonstrate that no major, irreversible degradation occurs up to around 70-80% SoC[39,40,65,66].”
A review of gas evolution in lithium ion batteries (2020, background): “It has been found that oxygen evolution is not dependent on cell potential but is reliant on the state of charge (SOC) and is onset at a SOC of 80% for NMC materials [40,43].”