Polyvinyl alcohol nanofiber reinforced Nafion membranes for fuel cell applications

By S. Mollá, V. Compañ. 2011

145 citations recorded by the source corpus.

Abstract This work has been focused on the preparation and characterization of composite membranes with thickness between 19 and 97 μm and containing Nafion ® infiltrated into a porous mat obtained by electrospinning of an aqueous solution of Poly vinyl alcohol (PVA). The mat was composed of PVA nanofibers with diameters between 200 and 300 nm, which were functionalized on their external surface with sulfonic acid groups in order to cooperate in the proton conductivity of Nafion ® . The proton conductivity of a composite membrane (47 μm thick) measured by impedance spectroscopy reached 0.022 S/cm at 70 °C and fully hydrated. This value is lower than the conductivity measured in the same conditions for a pristine Nafion ® cast membrane (46 μm), 0.032 S/cm. However, the performance of both membranes in Direct Methanol Fuel Cell tests was evaluated and showed comparable results. The proton conductivity of a series of cast Nafion ® membranes with thickness similar to those of the composite membranes was found to behave linearly thickness-dependent, while NAF/PVA composite membranes do not show such a linear behavior due to their heterogeneous composition. Nevertheless, the composite membrane presenting a thickness of 47 μm records the maximum peak conductivities at the whole temperature range. An intrinsic value for the activation energy of our cast Nafion ® membranes at fully hydrated conditions was estimated to be 7 kJ/mol.

Subfields: Automotive Engineering, Biomedical Engineering, Electrical and Electronic Engineering

View Paper: https://www.semanticscholar.org/paper/e29c7ead258dca67a2882b5d9974cb26c0bdc4e8

How researchers see this paper

The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.

1. Ying Ma
2. Weiping Zhou
3. Xiaoming Shi
4. Qian Ma
5. D. Bridges
6. A. Hu
7. Delong Ma

Citations in the corpus

• Electrospinning of nanofibers and their applications for energy devices (2015, methodology): “However, Nafion alone is difficult to electrospin and requires the presence of a high molecular weight carrier polymer such as PEO [102], poly(acrylic acid) (PAA) [103], or poly(vinyl alcohol) (PVA) [104] in the electrospinning solution due to its insolubility in alcohol/water solutions and in commo”