Dynamic and post-dynamic recrystallization under hot, cold and severe plastic deformation conditions
By Taku Sakai, A. Belyakov, R. Kaibyshev, H. Miura, J. Jonas. 2014
2,489 citations recorded by the source corpus.
Abstract The evolution of the new microstructures produced by two types of dynamic recrystallization is reviewed, including those brought about by severe plastic deformation (SPD). The microstructural changes taking place under these conditions and the associated mechanical behaviors are described. During the conventional discontinuous dynamic recrystallization (dDRX) that takes place at elevated temperatures, the new grains evolve by nucleation and growth in materials with low to medium stacking fault energies (SFE). On the other hand, new ultrafine grains can be produced in any material irrespective of the SFE by means of SPD at relatively low temperatures. These result from the gradual transformation of the dislocation sub-boundaries produced at low strains into ultrafine grains with high angle boundaries at large strains. This process, termed in situ or continuous dynamic recrystallization (cDRX), is still not perfectly understood. This is because many SPD methods provide data concerning the microstructural changes that take place but little information regarding the flow stress behavior. By contrast, multi-directional forging (MDF) provides both types of data concurrently. Recent studies of the deformation behavior of metals and alloys under SPD conditions, carried out using MDF as well as other SPD methods, are synthesized and the links between the microstructural and mechanical observations are examined carefully. Some models for grain formation under SPD conditions are discussed. Next, the post-dynamic recrystallization behavior, i.e. that of annealing after both dDRX and cDRX, is described. The differing annealing behaviors result from the differences in the natures of the deformed microstructures. Finally, an integrated recrystallization model for these phenomena, i.e. dynamic and static recrystallization of both the continuous and discontinuous types, is presented and discussed.
Subfields: Materials Chemistry, Mechanical Engineering, Mechanics of Materials
View Paper: https://www.semanticscholar.org/paper/da0e43a9dd82262a7cb62796f0aa4cb987681b15
How researchers see this paper
The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.
In Materials Chemistry
In Mechanical Engineering
Citations in the corpus
- “Self-sharpening” tungsten high-entropy alloy (2020, background): “Recently, DRX has been regarded as a potential physical origin for shear band formation [62 64], as the occurrence of DRX is accompanied by a sudden reduction of dislocation density that finally leads to an instant stress drop [49].”