Efficient propane low-temperature destruction by Co3O4 crystal facets engineering: Unveiling the decisive role of lattice and oxygen defects and surface acid-base pairs

By Yanfei Jian, Mingjiao Tian, Chi He, Jing-Fang Xiong, Zeyu Jiang, Huidong Jin, Lirong Zheng, Reem Albilali, Jian-Wen Shi. 2021

264 citations recorded by the source corpus.

Abstract Low-temperature degradation of short chain alkane is one of the greatest challenges of volatile organic compound purification. Here, rod-, sheet-, and cube-like Co3O4 (Co3O4-R, Co3O4-S, and Co3O4-C) with predominantly exposed (110), (111), and (100) facets respectively were fabricated. Co3O4-R presents excellent activity achieving 90 % of propane oxidized at just 195 °C owing to large amounts of lattice defects, oxygen vacancies and low coordinated Co atoms. Theoretical calculation reveals that Co3O4-R has the lowest formation energy of oxygen vacancy on (110) facet (Evo (110) =1.7 eV), which has a higher activation capacity for oxygen due to the largest O2 adsorption energy (−1.30 eV) and thus accelerates propane oxidation. Moreover, largest amount of lewis acid-base pairs existed in Co3O4-R polarizes substrate electron distribution and therefore accelerates the activation of C–H bonds. Electrophilic oxygen species (O22− or O−) caused the degradation of carbon skeleton and formed carboxylate intermediates before mineralized to CO2.

Subfields: Catalysis, Materials Chemistry

View Paper: https://www.semanticscholar.org/paper/d35a4cb7359d3e6a345a11de7f01b0182b4eaf98