How Much Oxygen Can a MXene Surface Take Before It Breaks?

By Ingemar Persson, J. Halim, T. Hansen, J. Wagner, V. Darakchieva, J. Palisaitis, J. Rosen, P. Persson. Advanced Functional Materials, 2020

160 citations recorded by the source corpus.

Tuning and tailoring of surface terminating functional species hold the key to unlock unprecedented properties for a wide range of applications of the largest 2D family known as MXenes. However, a few routes for surface tailoring are explored and little is known about the extent to which the terminating species can saturate the MXene surfaces. Among available terminations, atomic oxygen is of interest for electrochemical energy storage, hydrogen evolution reaction, photocatalysis, etc. However, controlled oxidation of the surfaces is not trivial due to the favored formation of oxides. In the present contribution, single sheets of Ti3C2Tx MXene, inherently terminated by F and O, are defluorinated by heating in vacuum and subsequentially exposed to O2 gas at temperatures up to 450 °C in situ, in an environmental transmission electron microscope. Results include exclusive termination by O on the MXene surfaces and eventual supersaturation (x > 2) with a retained MXene sheet structure. Upon extended O exposure, the MXene structure transforms into TiO2 and desorbs surface bound H2O and CO2 reaction products. These results are fundamental for understanding the oxidation, the presence of water on MXene surfaces, and the degradation of MXenes, and pave way for further tailoring of MXene surfaces.

Subfields: Electrical and Electronic Engineering, Materials Chemistry

View Paper: https://www.semanticscholar.org/paper/bddecf219b90a5a08e144a86ba02f64ad94ee273

How researchers see this paper

The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.

In Electrical and Electronic Engineering

In Materials Chemistry

Citations in the corpus

The world of two-dimensional carbides and nitrides (MXenes) (2021, background): “The physisorbed water can be removed at temperatures below 200°C, while the monolayer of chemisorbed water with hydrogen bonding to the surface may still remain intercalated in the MXene (33, 34), requiring vacuum annealing at temperatures reaching 500°C for removal (25, 34).”