Zero-valent iron and biochar composite with high specific surface area via K2FeO4 fabrication enhances sulfadiazine removal by persulfate activation

By Dongmei Ma, Yang Yang, Bing-feng Liu, Guojun Xie, Chuan Chen, N. Ren, D. Xing. 2021

204 citations recorded by the source corpus.

Abstract Zero-valent iron and biochar composite (ZVI/BC) is a prospective catalyst for activating persulfate and specific surface area (SSA) of ZVI/BC is one of the most important factors affecting its efficacy in the removal of environmental contaminants. However, the green fabrication of ZVI/BC with large SSA remains a challenge. In this study, ZVI/BC with a highly porous structure and large SSA fabricated by co-pyrolysis of K2FeO4 and bamboo was prepared and characterized. The large SSA stemmed from the catalytic and corrosive functions of K and the oxidation of K2FeO4 onto bamboo. ZVI/BC fabricated with 0.05 mol/L K2FeO4 (BC-Fe0.05) showed optimal sulfadiazine (SDZ) removal performance in the peroxydisulfate (PDS) activation system with complete removal after 10 min, as it showed the highest adsorptive ability of SDZ. Moreover, BC-Fe0.05 was able to remain stable after four cycles or 80 days of storage. Higher temperature, lower pH, and Cl− were beneficial to SDZ removal efficiency, whereas CO32– and HPO42− had inhibitory effects. Non-radical species (1O2) and radical species (SO4 −, OH, and O2 −) both contributed to SDZ degradation, and 1O2 was the most important reactive oxygen species. Four degradation pathways were proposed based on ten identified intermediates. Potential eco-toxicity analysis by ECOSAR suggested that most intermediates were less toxic than their parent compound. Overall, this study describes a green fabrication method for ZVI/BC with large SSA using K2FeO4 as the iron precursor. Generally, ZVI/BC with large SSA is an effective catalyst for activating persulfate to degrade antibiotics.

Subfields: Biomedical Engineering, Environmental Chemistry, Water Science and Technology

View Paper: https://www.semanticscholar.org/paper/b0ac74dc1feccff93e611d0ba5cc5a469e795752