Highly reusable visible light active hierarchical porous WO3/SiO2 monolith in centimeter length scale for enhanced photocatalytic degradation of toxic pollutants

By Surbhi Sharma, S. Basu. 2020

139 citations recorded by the source corpus.

Abstract To develop techniques like photocatalytic degradation of toxic-pollutants to reduce water pollution is essential as every human being has the right to have an access to safe water. Metal oxide monoliths have a huge significance regarding this due to their easy-to-separate nature. Porous WO3/SiO2 monoliths were synthesized by vacuum-impregnation of sodium tungstate in silica monoliths and calcination. The XRD spectra confirmed the successful formation of monolith and the morphological studies were done by FESEM exhibiting a connected porous network structure. The elemental-state and uniform elemental-distribution were analyzed by XPS and EDS. BET analysis showed that monoliths displayed multimodal porosity with pore-diameter of 0.70–14.71 nm and high surface area (82 m2/g). DRS revealed that the monolith had a narrow band gap (2.5 eV), which is suitable for visible light photocatalysis. The photocatalytic performance of monolith was estimated by degradation of model-pollutant methylene blue (MB) under visible-light illumination. High photocatalytic efficiency (91%) and rate constant (0.013 min−1) was observed at natural pH of the dye (pH 7.5). The effect of pH and catalyst concentration was explored which revealed that best degradation occurred at pH 3 (97.5%) and catalyst concentration 0.4 g/L (96%). The trapping experiments suggested that the holes were governing reactive-species in the reaction. The photocatalyst was reused for 5 consecutive cycles (80% degradation). The characterization-results of monolith after 2nd cycle of photodegradation explicated its stability. A colorless-pollutant (Imidacloprid) was also degraded to distinguish between direct and indirect photocatalysis. A comparative study was also done with reported catalysts in literature regarding MB degradation.

Subfields: Polymers and Plastics, Renewable Energy, Sustainability and the Environment

View Paper: https://www.semanticscholar.org/paper/af40783af7f919d999c5255816df5eea28b437d4