By Gaoming Zhu, Leyun Wang, Hao Zhou, Jinhui Wang, Yao Shen, Peng Tu, Hong Zhu, Wei Liu, P. Jin, Xiaoqin Zeng. International journal of plasticity, 2019

276 citations recorded by the source corpus.

Abstract Addition of a small amount of Ca improves the ductility of Mg alloys. However, the mechanism underlying this effect is not well understood. In this work, tensile testing of an extruded Mg−0.47 wt% Ca alloy was conducted inside a scanning electron microscope. Electron backscattered diffraction-based slip trace analysis was performed to study in-grain slip activities at 1%, 2%, 4%, 8%, and 16% tensile strain. While the majority of the grains were deformed by { 0001 } 11 2 _ 0 > basal slip, slip lines from { 1 1 _ 00 } prismatic planes and { 1 1 _ 01 } pyramidal I planes were also frequently observed, and their fractions increased with strain. Ex situ transmission electron microscopy indicated that the pyramidal I slip lines were associated with dislocations instead of dislocations. From Schmid factor analysis, the critical resolved shear stresses of prismatic slip and pyramidal slip are approximately twice that of basal slip in this Mg–Ca alloy. The enhanced activity of non-basal slip improved the material's ductility. Our first-principles calculations found that solute Ca atoms would reduce the unstable stacking fault energy for all slip modes.

Subfields: Biomaterials, Materials Chemistry, Mechanical Engineering

View Paper: https://www.semanticscholar.org/paper/ac5f7e2c1d8e4835f700f87dd918384a07dbb4b2