By Sheng-dan Liu, Bin Chen, Chengbo Li, Yun Dai, Yun-lai Deng, Xu-hu Zhang. 2015

146 citations recorded by the source corpus.

Abstract Electrochemical impedance spectroscopy and accelerated immersion testing results indicate that a lower quench rate leads to lower exfoliation corrosion resistance in 7055 aluminium alloy. The mechanism was discussed based on the change in grain boundaries microstructure and microchemistry due to slow quenching. Because of the increase of Zn and Mg content, grain boundary particles in the slowly-quenched specimens are more electrochemically active and tend to accelerate corrosion despite their large size and spacing; moreover the wide precipitates free zones depleted of solutes near grain boundaries tend to be more active as well and accelerate corrosion along grain boundaries.