Silver Nanowire Networks as Flexible, Transparent, Conducting Films: Extremely High DC to Optical Conductivity Ratios.

By S. De, Thomas M. Higgins, Philip E. Lyons, Evelyn M. Doherty, P. Nirmalraj, W. Blau, John Boland, Jonathan N. Coleman. ACS Nano, 2009

1,553 citations recorded by the source corpus.

We have used aqueous dispersions of silver nanowires to prepare thin, flexible, transparent, conducting films. The nanowires are of length and diameter close to 6.5 μm and 85 nm, respectively. At low thickness, the films consist of networks but appear to become bulk-like for mean film thicknesses above ∼160 nm. These films can be very transparent with optical transmittance reaching as high as 92% for low thickness. The transmittance (550 nm) decreases with increasing thickness, consistent with an optical conductivity of 6472 S/m. The films are also very uniform; the transmittance varies spatially by typically <2%. The sheet resistance decreases with increasing thickness, falling below 1 Ω/◻ for thicknesses above 300 nm. The DC conductivity increases from 2 × 10(5) S/m for very thin films before saturating at 5 × 10(6) S/m for thicker films. Similarly, the ratio of DC to optical conductivity increases with increasing thickness from 25 for the thinnest films, saturating at ∼500 for thicknesses above ∼160 nm. We believe this is the highest conductivity ratio ever observed for nanostructured films and is matched only by doped metal oxide films. These nanowire films are electromechanically very robust, with all but the thinnest films showing no change in sheet resistance when flexed over >1000 cycles. Such results make these films ideal as replacements for indium tin oxide as transparent electrodes. We have prepared films with optical transmittance and sheet resistance of 85% and 13 Ω/◻, respectively. This is very close to that displayed by commercially available indium tin oxide.

Subfields: Biomedical Engineering, Electrical and Electronic Engineering, Materials Chemistry

View Paper: https://www.semanticscholar.org/paper/a824a2686b0ef5ec6e6173ebf823410d99e7a493

How researchers see this paper

The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.

In Biomedical Engineering

In Electrical and Electronic Engineering

In Materials Chemistry

Citations in the corpus

Direct synthesis of highly conductive poly(3,4-ethylenedioxythiophene):poly(4-styrenesulfonate) (PEDOT:PSS)/graphene composites and their applications in energy harvesting systems (2014, background): “Highly conductive films using metal nanostructures [1–4], conductive polymers (CPs) [5], carbon-based materials [6], and hybrid materials [7], have attracted a great deal of attention for various applications such as transparent electrodes [8], solar cells [9], lightemitting diodes (LEDs) [8], and t”