Additive manufacturing of ultrafine-grained high-strength titanium alloys
By Duyao Zhang, D. Qiu, M. Gibson, Yufeng Zheng, H. Fraser, D. StJohn, M. Easton. Nature, 2019
934 citations recorded by the source corpus.
Additive manufacturing, often known as three-dimensional (3D) printing, is a process in which a part is built layer-by-layer and is a promising approach for creating components close to their final (net) shape. This process is challenging the dominance of conventional manufacturing processes for products with high complexity and low material waste1. Titanium alloys made by additive manufacturing have been used in applications in various industries. However, the intrinsic high cooling rates and high thermal gradient of the fusion-based metal additive manufacturing process often leads to a very fine microstructure and a tendency towards almost exclusively columnar grains, particularly in titanium-based alloys1. (Columnar grains in additively manufactured titanium components can result in anisotropic mechanical properties and are therefore undesirable2.) Attempts to optimize the processing parameters of additive manufacturing have shown that it is difficult to alter the conditions to promote equiaxed growth of titanium grains3. In contrast with other common engineering alloys such as aluminium, there is no commercial grain refiner for titanium that is able to effectively refine the microstructure. To address this challenge, here we report on the development of titanium–copper alloys that have a high constitutional supercooling capacity as a result of partitioning of the alloying element during solidification, which can override the negative effect of a high thermal gradient in the laser-melted region during additive manufacturing. Without any special process control or additional treatment, our as-printed titanium–copper alloy specimens have a fully equiaxed fine-grained microstructure. They also display promising mechanical properties, such as high yield strength and uniform elongation, compared to conventional alloys under similar processing conditions, owing to the formation of an ultrafine eutectoid microstructure that appears as a result of exploiting the high cooling rates and multiple thermal cycles of the manufacturing process. We anticipate that this approach will be applicable to other eutectoid-forming alloy systems, and that it will have applications in the aerospace and biomedical industries. Titanium–copper alloys with fully equiaxed grains and a fine microstructure are realized via an additive manufacturing process that exploits high cooling rates and multiple thermal cycles.
Subfields: Automotive Engineering, Materials Chemistry, Mechanical Engineering
View Paper: https://www.semanticscholar.org/paper/8bd2e6336b38743e71c2564d2f39dfc8160417da
How researchers see this paper
The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.
In Automotive Engineering
In Materials Chemistry
In Mechanical Engineering
Citations in the corpus
- Recent innovations in laser additive manufacturing of titanium alloys (2024, background): “Zhang et al [65] investigated the microstructure and mechanical properties of LDED Ti-x Cu (x = 3.5, 6.5 and 8.5 wt”
- Grain refinement of stainless steel in ultrasound-assisted additive manufacturing (2020, background): “conditions, including ultrasonic [17, 35, 36] and AM [37-39] conditions.”
- Material-structure-performance integrated laser-metal additive manufacturing (2021, background): “An example is laser-printed titanium-copper alloys having a high constitutional supercooling capacity, which offsets the negative effect of a laser-induced high thermal gradient and ensures a complete columnar-to-equiaxed transition (126).”