Influence of silver ion reduction on electrical modulus parameters of solid polymer electrolyte based on chitosan- silver triflate electrolyte membrane

By S. B. Aziz, Zurina Zainal Abidin, A. Arof. 2010

206 citations recorded by the source corpus.

The electric modulus properties of solid polymer electrolyte based on chitosan: AgCF3SO3 from 303 to 393 K have been investigated by using impedance spectroscopy. The shift of the M" peak spectra with frequeny depends on the dissociation and association of ions. The lowest conductivity relaxation time τσ, was found for the sample with the highest conductivity. The real part of electrical modulus shows that the material is highly capacitive. The asymmetric peak of the imaginary part of electric modulus M", predicts a non Debye type relaxation. The distribution of relaxation times was indi- cated by a deformed arc form of Argand plot. The increase of Mand M" values above 358 K can be attributed to the trans- formation of silver ions to silver nanoparticles. The complex impedance plots and ultraviolet-visible (UV-vis) absorption spectroscopy indicate the temperature dependent of silver nanoparticles in chitosan-silver triflate solid electrolyte. The for- mation of silver nanoparticles was confirmed by transmission electron microscopy (TEM). The scaling behavior of M" spectra shows that the dynamical relaxation processes is temperature independent for aparticular composition. The β expo- nent value indicate that the conductivity relaxation is highly non exponential.

Subfields: Electrical and Electronic Engineering, Polymers and Plastics

View Paper: https://www.semanticscholar.org/paper/7f641053a56c406d6ef3ec7a38a0c73b2a76c989