Ultrafast gelling using sulfonated lignin-Fe3+ chelates to produce dynamic crosslinked hydrogel/coating with charming stretchable, conductive, self-healing, and ultraviolet-blocking properties

By Qinhua Wang, Xiaofeng Pan, Changmei Lin, Xiaojuan Ma, S. Cao, Y. Ni. 2020

211 citations recorded by the source corpus.

Abstract Developing an ecological and economical method for fabrication and application of polymer hydrogels is important for the hydrogel/coating electronics. Here, a dynamic oxidation and coordination system composed of sulfonated lignin (SL) and Fe3+ was introduced to assemble multifunctional Fe-SL-g-polyacrylic acid (PAA) hydrogel at 20 ℃ in a time scale of minutes instead of hours. The SL-Fe3+ system can rapidly activate the ammonium persulfate (APS, initiator), and then it instantaneously provides abundant semiquinone and hydroxyl radicals to accelerate the formation of polymer chains. Moreover, the functional SL-Fe3+ chelates can also reversibly crosslink the polymer chains to form multifunctional hydrogels. Surprisingly, the resultant hydrogel obtained charming extension ratio (up to 1680%), conductivity (up to 7.0 × 10-2 S·m−1), and adhesive strength (up to 36.4 kPa). This technology was also applied to rapidly fabricate a transparent (up to 81%, thickness: 2 mm), UV-blocking (up to 99.7%, thickness: 2 mm), adhesive, and conductive hydrogel coating on substrates. Besides, the dynamic coordination inside the hydrogel imparts desirable self-healing capabilities to damaged network, with up to 98.5% recovery in conductivity and 85.7% in extension ratio. In short, this technology based on the sustainable SL-Fe3+ system greatly facilitates the rapid and low-cost preparation of multifunctional hydrogel/coatings, which have promising industrial applications in human–machine electronics.

Subfields: Biomedical Engineering, Molecular Medicine, Polymers and Plastics

View Paper: https://www.semanticscholar.org/paper/7e6329918ca8ef97f8d01b399169d48d10ef27eb