Degradation of polypropylene (PP) during multiple extrusions: Thermal analysis, mechanical properties and analysis of variance

By H. M. Costa, V. D. Ramos, Márcia G. Oliveira. 2007

200 citations recorded by the source corpus.

The effects of repetitive extrusion cycles at different die temperatures in a single screw extruder were investigated by thermal analysis (degree of crystallinity (χc), heat of fusion (ΔHm), melting temperature (Tm) and the onset melting temperature (Tonset,m)) and mechanical properties (tensile and impact strength). Also, analysis of variance (ANOVA) and response surface methodology (RSM) were employed for modeling and analysis of the mechanical property results. Thermal analysis verified an increase for χc and ΔHm with a continuous reduction in the Tm and Tonset,m values with increase of die temperature and/or cycles of extrusion. For mechanical properties, the observed degradation process only slightly affects the small strain properties (yield stress and modulus) and impact strength. Break properties (break stress, break strain and energy to break) were reduced significantly by the experimental conditions adopted. According to ANOVA and RSM, the degradation process was occasioned more by high shear rate (repetitive number of cycles) than by high processing temperatures.

Subfields: Fluid Flow and Transfer Processes, Polymers and Plastics

View Paper: https://www.semanticscholar.org/paper/7c7c561632cc94aee2a8d993694c2e96a01796f6

Citations in the corpus

• Use of macro plastic fibres in concrete: A review (2015, background): “However, 287 it swells when exposed to aliphatic and aromatic hydrocarbons and by halogenated 288 hydrocarbons [80].”