Carbonation resistance of cements containing supplementary cementitious materials and its relation to various parameters of concrete

By Vineet Shah, Shashank Bishnoi. Construction and Building Materials, 2018

144 citations recorded by the source corpus.

Abstract In this study, the carbonation resistance of cements containing supplementary cementitious materials (SCMs) exposed to carbon dioxide concentrations of 1% and 3%, relative humidity of 40%, 60% and 80% and temperature of 27 °C and 45 °C at two different water to cement ratio is investigated. The carbonation performance of concrete samples placed in accelerated conditions is compared to that of concrete samples exposed to natural conditions. The comparison of carbonation coefficients of concrete exposed to different environmental conditions indicates that the rate of carbonation is primarily governed by the extent of clinker replacement, relative humidity and water to cement ratio. Concrete mixes with slag showed better carbonation resistance as compared to mixes containing other SCMs. No specific correlation can be observed between the carbonation coefficients and physical parameters of concrete (compressive strength and porosity), however, a reasonable correlation is observed between carbonation coefficients and chemical parameters (Total alkali content, reserve alkalinity and pH). An empirical equation is developed to estimate the carbonation depth for different cements for wide range of exposure conditions.

Subfields: Civil and Structural Engineering, Materials Chemistry

View Paper: https://www.semanticscholar.org/paper/75dbaff05b7d869ccdb1fc7ecdbac12295e34c91