Strengthening mechanisms in magnesium alloys containing ternary I, W and LPSO phases

By N. Tahreen, Dingfei Zhang, F. Pan, X. Jiang, Dong-yang Li, Daolun L. Chen. Journal of Materials Science & Technology, 2017

150 citations recorded by the source corpus.

Abstract This study was aimed at identifying underlying strengthening mechanisms and predicting the yield strength of as-extruded Mg-Zn-Y alloys with varying amounts of yttrium (Y) element. The addition of Y resulted in the formation of ternary I (Mg3YZn6), W (Mg3Y2Zn3) and LPSO (Mg12YZn) phases which subsequently reinforced alloys ZM31 + 0.3Y, ZM31 + 3.2Y and ZM31 + 6Y, where the value denoted the amount of Y element (in wt%). Yield strength of the alloys was determined via uniaxial compression testing, and grain size and second-phase particles were characterized using OM and SEM. In-situ high-temperature XRD was performed to determine the coefficient of thermal expansion (CTE), which was derived to be 1.38 × 10−5 K−1 and 2.35 × 10−5 K−1 for W and LPSO phases, respectively. The individual strengthening effects in each material were quantified for the first time, including grain refinement, Orowan looping, thermal mismatch, dislocation density, load-bearing, and particle shearing contributions. Grain refinement was one of the major strengthening mechanisms and it was present in all the alloys studied, irrespective of the second-phase particles. Orowan looping and CTE mismatch were the predominant strengthening mechanisms in the ZM31 + 0.3Y and ZM31 + 3.2Y alloys containing I and W phases, respectively, while load-bearing and second-phase shearing were the salient mechanisms contributing largely to the superior yield strength of the LPSO-reinforced ZM31 + 6Y alloy.

Subfields: Biomaterials, Mechanical Engineering

View Paper: https://www.semanticscholar.org/paper/6b6ab2436cecf6dc531a762390d4db5515fca503