Molten chloride salts for next generation concentrated solar power plants: Mitigation strategies against corrosion of structural materials

By Wenjin Ding, Haofan Shi, A. Jianu, Yanlei Xiu, A. Bonk, A. Weisenburger, Thomas Bauer. Solar Energy Materials and Solar Cells, 2019

187 citations recorded by the source corpus.

Abstract Molten chloride salts are promising advanced high-temperature (400–800 °C) thermal energy storage (TES) and heat transfer fluid (HTF) materials in next generation concentrated solar power (CSP) plants for higher energy conversion efficiencies. However, severe corrosion of structural materials in contact with molten chloride salts is one of the most critical challenges limiting their applications at elevated temperatures. In this work, two corrosion mitigation strategies are investigated to alleviate the hot corrosion of structural materials in molten chloride salts: (1) adding corrosion inhibitor and (2) using a Fe-Cr-Al alloy with a protective alumina layer on the surface after pre-oxidation. Three commercial high temperature Fe-Cr-Ni alloys (SS 310, Incoloy® 800 H and Hastelloy® C-276) were exposed to molten MgCl2-NaCl-KCl (60–20–20 mol%) mixed salts with 1 wt% Mg as corrosion inhibitor, for 500 h at 700 °C under inert atmosphere. By addition of the Mg inhibitor, the corrosion rates of the studied alloys were found to be significantly reduced, more precisely by ~ 83% for SS 310, ~ 70% for In 800 H and ~ 94% for Ha C-276 compared with the exposure tests without Mg addition. The corrosion mitigation mechanism of Fe-Cr-Ni based alloys in molten chloride salts by adding Mg is discussed based on corrosion thermodynamics. To assess the second mitigation strategy two pre-oxidized alumina forming Fe-Cr-Al alloys were exposed to the same molten chloride salts without Mg corrosion inhibitor under the same conditions. It is observed that the adherent alumina scales can effectively inhibit the dissolution of Cr and Fe and the bulk penetration of corrosive impurities. Overall, both strategies offer enormous potential for enhancing the expected lifetime of commercial alloys in molten chloride salts.

Subfields: Mechanical Engineering, Renewable Energy, Sustainability and the Environment

View Paper: https://www.semanticscholar.org/paper/62e276ed94fca70b184b34b5ba2368c7ed831256

How researchers see this paper

The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.

In Mechanical Engineering

  1. Wenjin Ding
  2. Thomas Bauer

In Renewable Energy, Sustainability and the Environment

  1. Wenjin Ding
  2. Thomas Bauer

Citations in the corpus