Correlation between degree of crystallinity, morphology, glass temperature, mechanical properties and biodegradation of poly (3-hydroxyalkanoate) PHAs and their blends

By A. M. El-hadi, R. Schnabel, E. Straube, G. Müller, S. Henning. 2002

413 citations recorded by the source corpus.

Abstract Bacterial thermoplastic polyesters poly (3-hydroxyalkanoate) PHAs are produced by the fermentation of renewable materials, such as sugars or molasses. The pure homopolymer, PHB, and pure copolymer (3-HBP-CO-HV) (88:12) are brittle materials. PHB or PHB/V are mixed with other biodegradable materials to improve their mechanical properties. The aim is to develop biodegradable polymers of PHB-base with improved mechanical properties, such as fracture stress (27–18 MPa), strain (400–660%), impact strength and long-term stability, and to compare them with PE, PP and PET. When nucleating agents are added, smaller spherulites are formed, thus improving the mechanical properties. The mechanical properties of PHB and its blends are related to processing conditions, morphology, crystallinity and glass transition. The blends are ductile polymers with plastic deformation (necking). They are biodegraded in aerobic tests, under compost conditions in soil and water, and many pores are to be found on the surface. The blends are degraded more easily in the aerobic test, i.e. in the river water and compost, than in the soil.

Subfields: Biomaterials, Polymers and Plastics

View Paper: https://www.semanticscholar.org/paper/57f890724a9022b098482371a9670e522be282df

How researchers see this paper

The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.

In Biomaterials

1. L. Avérous
2. Andrea Lazzeri
3. P. Cinelli
4. V. Alvarez
5. Koon-Yang Lee
6. Elodie Bugnicourt
7. E. Pollet
8. P. Halley

In Polymers and Plastics

1. L. Avérous
2. Andrea Lazzeri
3. P. Cinelli
4. V. Alvarez
5. Koon-Yang Lee
6. Elodie Bugnicourt

Citations in the corpus

• Mechanical properties of CF-reinforced PLA parts manufactured by fused deposition modeling (2019, background): “between crystalline fraction and mechanical properties of PLA processed by conventional methods.(30,31) Improvement in tensile strength and elastic modulus for these samples is still essential while the amorphous region remains significant.”
• Polymer biodegradation: mechanisms and estimation techniques. (2008, background): “Under Tg (glassy state), the formation of spherulites may take place, generating interspherulitic cracks and the brittleness of the thermoplastics polymers (El-Hadi et al., 2002).”
• Measurements of the mechanical response of unidirectional 3D-printed PLA (2017, background): “However, the 3D-printed and injection-moulded samples, of relatively high crystallinity, are much more brittle and moderately weaker than the filaments [34,35].”
• Biodegradable Multiphase Systems Based on Plasticized Starch: A Review (2004, background): “The kinetics of enzymatic degradation is variable according to the crystallinity, the structure,([5,31]) and then, to the processing history.”
• Polyhydroxyalkanoate (PHA): Review of synthesis, characteristics, processing and potential applications in packaging (2014, background): “2 GPa and 25 MPa [13].”