By T. Ojeda, A. P. Freitas, K. Birck, Emilene Dalmolin, R. Jacques, F. Bento, F. Camargo. 2011
245 citations recorded by the source corpus.
High density polyethylene (HDPE), linear low density polyethylene (LLDPE), and isotactic polypropylene (PP) containing antioxidant additives at low or zero levels were extruded and blown moulded as films. An HDPE/LLDPE commercial blend containing a pro-oxidant additive (i.e., an oxo-biodegradable blend) was taken from the market as supermarket bag. These four polyolefin samples were exposed to natural weathering for one year during which their structure and thermal and mechanical properties were monitored. This study shows that the real durability of olefin polymers may be much shorter than centuries, as in less than one year the mechanical properties of all samples decreased virtually to zero, as a consequence of severe oxidative degradation, that resulted in substantial reduction in molar mass accompanied by a significant increase in content of carbonyl groups. PP and the oxo-bio HDPE/LLDPE blend degraded very rapidly, whereas HDPE and LLDPE degraded more slowly, but significantly in a few months. The main factors influencing the degradability were the frequency of tertiary carbon atoms in the chain and the presence of a pro-oxidant additive. The primary (sterically hindered phenol) and secondary (phosphite) antioxidant additives added to PP slowed but did not prevent rapid photo-oxidative degradation, and in HDPE and LLDPE the secondary antioxidant additive had little influence on the rate of abiotic degradation at the concentrations used here.
Subfields: Biomaterials, Pollution, Polymers and Plastics
View Paper: https://www.semanticscholar.org/paper/5443dac576ab33bd2a55c0e9ab4b96472c16202b
How researchers see this paper
The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.
In Biomaterials
In Pollution
- A. Andrady
- A. Koelmans
- Colin R. Janssen
- Richard C. Thompson
- P. Ryan
- L. Van Cauwenberghe
- T. Galloway
- A. Lusher
In Polymers and Plastics
Citations in the corpus
- Persistence of Plastic Litter in the Oceans (2015, methodology): “While weathering related oxidative mechanisms for polyolefins (PE and PP) are well known (Ojeda 2011), the concurrent embrittlement of the material has not been adequately studied.”