Effect of alkali cation type on strength endurance of fly ash geopolymers subject to high temperature exposure
By Mukund Lahoti, K. Wong, K. Tan, E. Yang. Materials & Design (1980-2015), 2018
153 citations recorded by the source corpus.
Abstract Choice of alkali cation in mix design of geopolymers is critical for their thermal performance. However, the influence of alkali cation type on strength endurance of geopolymers subject to high temperature exposure and the underlying governing mechanisms have not been studied. This study investigated the effects of alkali cation type on high temperature response of fly ash geopolymers aiming towards structural applications. In-depth investigation was carried out to discover the underlying mechanisms governing the strength endurance of fly ash geopolymers subject to high temperature exposure and its correlation with their volume stability and chemical stability. Results showed that potassium geopolymer exhibited significant strength enhancement (30–40%) and sodium geopolymer displayed reduced strength (10%), and the strength of mixed sodium and potassium geopolymer remained unchanged after exposure to elevated temperature. While the binders were chemically stable without deterioration and formation of new crystal phases after high temperature exposure, the volume stability varied with the type of alkali cation used. Formation of cracks and gel densification due to shrinkage, and healing of micro-cracks and change of pore sizes due to sintering were identified as responsible mechanisms at different temperature ranges. While crack development and enlargement of pores lowered the strength, densification of matrix and healing of micro-cracks favored strength gain. These competing mechanisms determine the strength endurance of geopolymers depending on the type of alkali cation used. Overall, it shows that geopolymers can be tailored, such that stable (or even enhanced) strengths upon thermal exposure are realized, for structural applications.
Subfields: Civil and Structural Engineering, Materials Chemistry
View Paper: https://www.semanticscholar.org/paper/51fb2949aabaa0d68915ebc3217e81601169a9be
How researchers see this paper
The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.
In Civil and Structural Engineering
In Materials Chemistry
Citations in the corpus
- Thermal and Mechanical Properties of Geopolymers Exposed to High Temperature: A Literature Review (2020, background): “[87] found that the compressive strength of potassium-based FA geopolymers increased at temperatures exposed to 500°C, while the strength of sodium-based geopolymers decreased.”
- Fire Resistance Behaviour of Geopolymer Concrete: An Overview (2021, methodology): “[105] The geopolymer with potassium was substantially amended (30–40%) as well as the geopolymer made with sodium was declined (10%) and after exposure to elevated temperatures, the strength of a mixed sodium and of a potassium geopolymer remained unaffected.”