Epitaxial growth of topological insulator Bi2Se3 film on Si(111) with atomically sharp interface

By N. Bansal, Yong Seung Kim, Eliav Edrey, M. Brahlek, Y. Horibe, K. Iida, M. Tanimura, Guohong Li, T. Feng, H. Lee and 3 more. 2011

190 citations recorded by the source corpus.

Abstract Atomically sharp epitaxial growth of Bi 2 Se 3 films is achieved on Si(111) substrate with molecular beam epitaxy. Two-step growth process is found to be a key to achieve interfacial-layer-free epitaxial Bi 2 Se 3 films on Si substrates. With a single-step high temperature growth, second phase clusters are formed at an early stage. On the other hand, with low temperature growth, the film tends to be disordered even in the absence of a second phase. With a low temperature initial growth followed by a high temperature growth, second-phase-free atomically sharp interface is obtained between Bi 2 Se 3 and Si substrate, as verified by reflection high energy electron diffraction (RHEED), transmission electron microscopy (TEM) and X-ray diffraction. The lattice constant of Bi 2 Se 3 is observed to relax to its bulk value during the first quintuple layer according to RHEED analysis, implying the absence of strain from the substrate. TEM shows a fully epitaxial structure of Bi 2 Se 3 film down to the first quintuple layer without any second phase or an amorphous layer.

Subfields: Atomic and Molecular Physics, and Optics, Materials Chemistry

View Paper: https://www.semanticscholar.org/paper/5017024649f4d7b8ceff02e4ee0695a1c1eb60ec

Citations in the corpus