Effects of nitrogen content on microstructures and mechanical properties of (AlCrTiZrHf)N high-entropy alloy nitride films

By Panpan Cui, Wei Li, Ping Liu, Kecheng Zhang, Fengcang Ma, Xiaohong Chen, Rui Feng, P. K. Liaw. Journal of Alloys and Compounds, 2020

148 citations recorded by the source corpus.

Abstract The (AlCrTiZrHf)N high-entropy alloy nitride films were synthesized by reactive magnetron sputtering. The effects of different N2 flow rates on the microstructures and mechanical properties of (AlCrTiZrHf)N films were studied by the X-ray diffraction (XRD), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), nanoindentation, coating friction and wear tester. The results show that the AlCrTiZrHf high-entropy alloy film presents an amorphous state. With the increase of the N2 flow rate, the (AlCrTiZrHf)N high-entropy alloy nitride films transform to a face-centered-cubic (FCC) structure. When the N2:Ar ratio is 5:4, the hardness and elastic modulus of the films reach 33.1 GPa and 347.3 GPa, respectively. The strengthening effect is mainly attributed to the formation of saturated metal-nitride phases and the solid-solution strengthening of various elements. Meanwhile, the (AlCrTiZrHf)N film exhibits the low friction coefficient and superior wear resistance. Based on the excellent properties of high-entropy alloy nitride films, the (AlCrTiZrHf)N film presents a potential application in protective coating.

Subfields: Materials Chemistry, Mechanical Engineering, Mechanics of Materials

View Paper: https://www.semanticscholar.org/paper/4a85a128d3152e05bfc4fbf034f1c9287d3c8af4