Structure and morphology of self-assembled 3-mercaptopropyltrimethoxysilane layers on silicon oxide

By Minghui Hu, Suguru Noda, T. Okubo, Y. Yamaguchi, H. Komiyama. 2001

160 citations recorded by the source corpus.

Abstract Self-assembled 3-mercaptopropyltrimethoxysilane (MPTMS, (CH3O)3SiCH2CH2CH2SH) layers on hydroxyl-terminated silicon oxide (SiO2) were prepared at MPTMS concentrations ranging from 5×10−3 to 4×10 −2 M . The surface structure and morphology of MPTMS layers were characterized by X-ray photoelectron spectroscopy (XPS), contact angle measurements, scanning electron microscopy (SEM), and atomic force microscopy (AFM). We found that the MPTMS layers on SiO2 consisted of dispersed domains 20–200 nm in diameter, instead of continuous, flat monolayers. With increasing MPTMS concentration, the domain shape changed from flat to steep. Flat domains were composed of well-ordered monolayers with thiol headgroups uniformly distributed on the uppermost surface, whereas steep domains were composed of disordered polymers with randomly distributed thiol headgroups on the uppermost surface. These results indicate that MPTMS molecules show good self-assembly at an MPTMS concentration of 5×10 −3 M , but not above this concentration. The effect of MPTMS concentration on the structure and morphology of MPTMS layers might be due to the competition between self-polymerization and surface dehydration reactions, which depends on the trace quantity of water in the solvent and on the SiO2 surface. Our research further indicates that MPTMS and water concentrations are the controlling parameters for preparing well-ordered, self-assembled MPTMS monolayers on SiO2.

Subfields: Biomedical Engineering, Electrical and Electronic Engineering, Surfaces, Coatings and Films

View Paper: https://www.semanticscholar.org/paper/2b8a8061e4f1beba571132f7845ec8bc043a36bf

How researchers see this paper

The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.

1. D. Balköse
2. F. Tihminlioglu
3. D. Metin
4. S. Ülkü

Citations in the corpus

• The effect of interfacial interactions on the mechanical properties of polypropylene/natural zeolite composites (2004, background): “The contact angles of amino functional and mercapto silane coupling agents having terminal functional groups such as H2N– and HS– are higher than that of MTES, which has no functional group, because the introduction of a polar terminal functional group causes the formation of more ordered layers aro”