Selective laser melting of AlSi10Mg: Influence of post-processing on the microstructural and tensile properties development

By U. Tradowsky, J. White, R. M. Ward, N. Read, Walter Reimers, Moataz M. Attallah. 2016

317 citations recorded by the source corpus.

Abstract The study looks into the impact of thermal post-processing using Hot Isostatic Pressing (HIPping) and/or T6-peak aging treatment, post-process machining, as well as the build orientation on the microstructural and mechanical properties development in AlSi10Mg alloy fabricated using Selective Laser Melting (SLM). The builds contained fine columnar grains, with a fine Si-enriched cellular dendritic network, resulting in tensile strengths exceeding the castings. To elucidate the as-fabricated microstructure and strength, thermal modelling was employed, predicting cooling rates of 105–106 °C/s. Voids, mostly due to oxide films, were observed using Micro-CT in the as-fabricated condition. HIPping collapsed most voids, showing virtually no trace even after a further T6 treatment. Generally, the tensile properties of the majority of conditions were significantly better than in the cast + T6 equivalent alloy. Post-process machining was also found to improve the strength (compared to the as-fabricated surface). However, HIPping + T6 allowed the builds to achieve the required tensile properties, without surface machining. By assessing the influence of powder recycling, it was found that the void content linked to oxide layer formation increased following powder recycling, resulting in a drop in tensile properties. The interaction between the microstructure, surface condition, thermal post-processing, and fracture mode is discussed.

Subfields: Automotive Engineering, Mechanical Engineering

View Paper: https://www.semanticscholar.org/paper/226f6c824027c1f48410f9d6b5cc8e6204ad0deb

How researchers see this paper

The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.

In Automotive Engineering

In Mechanical Engineering

Citations in the corpus

3D printing of Aluminium alloys: Additive Manufacturing of Aluminium alloys using selective laser melting (2019, methodology): “[166] adopted the approach of reducing porosity in post-processing by applying a hot isostatic pressing (HIP) treatment to the SLM parts.”