Additive manufacturing of bio-inspired multi-scale hierarchically strengthened lattice structures

By Chao-lin Tan, Jihang Zou, Sheng Li, P. Jamshidi, A. Abena, A. Forsey, R. Moat, Khamis Essa, Minshi Wang, K. Zhou and 1 more. International journal of machine tools & manufacture, 2021

158 citations recorded by the source corpus.

Abstract The next-generation medical implants require locally customised biomechanical behaviour to echo the properties of hard tissues, making additive manufacturing (AM) an ideal route due to its superior manufacturing flexibility. AM of titanium alloys with designed porosity is the mainstream for artificial implants, which, however, hardly balance the strength-modulus combination. Here a martensitic TiNi biomaterial with low modulus and asymmetric mechanical behaviour that mimics human bones is explored. TiNi functionally graded lattice structure (FGLS) is bio-inspired by bone architecture and processed by AM. Bio-inspired FGLS shows much higher strength and ductility than the uniform lattice despite having an equivalent structural porosity. Post-process heat-treatments alter the microstructure and result in a multi-scale hierarchically strengthened behaviour in FGLS, offering one of the highest specific strengths (about 70 kN m/kg) among porous biometals, while keeping a low specific modulus and reasonable ductility. Besides, the deformation behaviour of FGLS is in-situ monitored, which, together with microscopic observations, reveal a multi-scale failure mechanism. The bio-inspired FGLS shows better biomechanical compatibility than the uniform lattice, including density, tension/compression asymmetry, modulus, and strength. The findings highlight the ability of AM in tailoring a modulus-strength-ductility trade-off through bio-inspired multi-scale hierarchical structure design.

Subfields: Biomedical Engineering, Materials Chemistry, Mechanical Engineering

View Paper: https://www.semanticscholar.org/paper/195edc84e7c88a1c331d99505b830bc826fa8842

How researchers see this paper

The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.

In Mechanical Engineering

1. Jinliang Zhang
2. B. Song
3. Yusheng Shi

Citations in the corpus

• Laser powder bed fusion additive manufacturing of NiTi shape memory alloys: a review (2023, background): “The unique characteristics have enabled the extensive application of NiTi products in various fields, such as actuators [10], electrical devices [11], biomedical [12], and aerospace [13].”