Simultaneous nitrogen doping and reduction of graphene oxide.

By Xiaoling Li, Hailiang Wang, J. Robinson, Hernan Sanchez, G. Diankov, Hongjie Dai. Journal of the American Chemical Society, 2009

1,700 citations recorded by the source corpus.

We developed a simple chemical method to obtain bulk quantities of N-doped, reduced graphene oxide (GO) sheets through thermal annealing of GO in ammonia. X-ray photoelectron spectroscopy (XPS) study of GO sheets annealed at various reaction temperatures reveals that N-doping occurs at a temperature as low as 300 degrees C, while the highest doping level of approximately 5% N is achieved at 500 degrees C. N-doping is accompanied by the reduction of GO with decreases in oxygen levels from approximately 28% in as-made GO down to approximately 2% in 1100 degrees C NH(3) reacted GO. XPS analysis of the N binding configurations of doped GO finds pyridinic N in the doped samples, with increased quaternary N (N that replaced the carbon atoms in the graphene plane) in GO annealed at higher temperatures (> or = 900 degrees C). Oxygen groups in GO were found responsible for reactions with NH(3) and C-N bond formation. Prereduced GO with fewer oxygen groups by thermal annealing in H(2) exhibits greatly reduced reactivity with NH(3) and a lower N-doping level. Electrical measurements of individual GO sheet devices demonstrate that GO annealed in NH(3) exhibits higher conductivity than those annealed in H(2), suggesting more effective reduction of GO by annealing in NH(3) than in H(2), consistent with XPS data. The N-doped reduced GO shows clearly n-type electron doping behavior with the Dirac point (DP) at negative gate voltages in three terminal devices. Our method could lead to the synthesis of bulk amounts of N-doped, reduced GO sheets useful for various practical applications.

Subfields: Biomedical Engineering, Electrical and Electronic Engineering, Materials Chemistry

View Paper: https://www.semanticscholar.org/paper/1449ea450a68ee30edd1887807be2b42bf332999

How researchers see this paper

The researchers whose trusted networks rank it highest, strongest advocate first. Every researcher gets a different order.

In Biomedical Engineering

In Electrical and Electronic Engineering

In Materials Chemistry

Citations in the corpus

Unveiling the active sites of graphene-catalyzed peroxymonosulfate activation (2016, background): “S2 and Table S2 illustrate that most of the carboxyl groups (eCOOH) were eliminated at 300 C, while thermal decomposition of kenotic and hydroxyl groups requires higher annealing temperature (>500 C) [29].”
The reduction of graphene oxide (2012, methodology): “As a result, annealing reduction is usually carried out in vacuum [55], or an inert [72] or reducing atmosphere [35,72,75,77].”